SINTESIS KOMPOSIT BIOPLASTIC BERBAHAN DASAR TEPUNG TAPIOKA DENGAN PENGUAT SERAT BAMBU
(1) Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Negeri Makassar Jl. Daeng Tata Raya, Makassar 90223
(2) Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Negeri Makassar Jl. Daeng Tata Raya, Makassar 90223
(3) Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Negeri Makassar
(*) Corresponding Author
DOI: https://doi.org/10.35580/jspf.v11i2.1486
Abstract
This research study abaout plastic manufacture which can be decomposed by bacteria and other decomposers so that good for environment (bioplastic). The Study examines the manufacture of plastics which can be decomposed by bacteria and other decomposers that environmentally friendly (bioplastic) using starch from cassava starch (tapioca flour) as the base material and glycerin+water as a plasticizer, and bamboo fiber as reinforcement. Based on the variation of glycerin, the highest tensile strength obtained at the starch composition 6 grams and 1.5 grams of glycerin before added the fiber 0,039 MPa and 0068 MPa after fiber is added, the value of Young's modulus of 0.90 GPa before adding fiber and 0.96 GPa after added fiber. The microstructure characterization results bioplastic composites showed good bonding between the matrix and fiber. However, there is damage to the bond after the burial. This is caused by the decomposition of starch bioplastic composites when buried in the soil (degradation). Based bio-degradibility test shows that the degradation time bioplastic that is 2 days. In addition, the results of XRD can be seen that bioplastic is semi amorphous.
Penelitian ini mengkaji mengenai pembuatan plastik yang dapat terurai oleh bakteri atau pengurai lainnya sehingga bersifat ramah lingkungan (bioplastic).Pembuatan bioplastic ini memanfaatkan pati dari pati singkong (Tepung Tapioka) sebagai bahan dasar dan gliserin+air sebagai plastisizer, serta serat bambu sebagai penguat. Berdasarkan variasi gliserin yang dilakukan, diperoleh kuat tarik tertinggi pada komposisi pati 6 gram dan gliserin 1,5 gram yaitu 0,039 MPa sebelum ditambahkan serat dan 0.068 MPa setelah ditambahkan serat, dengan nilai Modulus Young 0,90 GPa sebelum ditambahkan serat dan 0.96 GPa setelah ditambahkan serat. Hasil karakterisasi Struktur mikro komposit bioplastic menunjukkan adanya ikatan yang baik antara matriks dan serat.Namun, terjadi kerusakan ikatan setelah dilakukan pemendaman.Ini diakibatkan karena terjadinya penguraian pada pati saat komposit bioplastic dipendam dalam tanah (degradasi).Berdasarkan uji biodegradibilitas, diperoleh waktu degradasi sampel bioplastic yaitu mulai dari 2 hari. Selain itu, dari hasil XRD dapat dilihat bahwa bioplastic bersifat semi amorf.
Kata Kunci: komposit bioplastic, serat bambu, tepung tapioka
Full Text:
PDFReferences
Aufari, Afif. M. 2013. Pemurnian Crude Glycerine Melalui Roses Bleaching dengan Menggunakan Karbon Aktif. Jurnal Teknik Kimia USU, Vol. 2, No. 1, hal. 45.
Charles, A.H. 1999. Modern Plastic Handbook. Mc-Graw-Hill, Lutherville: Maryland.
Deswita, dkk. 2010. Sintesis dan Karakterisasi Polimer Komposit Polipropilen dengan Filler Tepung Tapioka untuk Bahan Kemasan. Indonesian Journal of Materials Science, Vol. 12, No. 1, hal 28.
Ganesh. S. 2014. Furnishing of BioPlastics from the Agrobased Polymer and Thermoplastic Strach Based Materials. SSRG International Journal of Polymer and Textile Engineering (SSRG-IJPTE), Vol. 1, hal 2.
Gaylord, M. 1974. Reinforced Plastics, Theory and Practise, 2nd edition. Massachusets: Chaner Books.
Gibson, R.F. 1994. Principles of Composite Material Mechanism.New York:Mc- Graw-Hill.Inc.
Murtingrum, dkk. 2012. Karakterisasi Umbi dan Pati Lima Kultur Ubi Kayu (Manihot Esculents). Jurnal agroteknologi, Vol. 3, No. 1, hal. 1-3.
Novita, dkk. 2013. Pengaruh Penggunaan Pati ganyong, Tapioka, dan Mocaf sebagai Bahan Subtitusi terhadap Sifat Fisik Mie Jagung. Jurnal Agritech, Vol. 33, No. 4, hal. 392.
Ochi, Shinji. 2012. Tensile Properties of Bamboo Fiber Reinforced iodegradable Plastics. International Journal of Composite Materials, Vol. 2, hal 3.
Subaer. 2012. Pengantar Fisika Polimer. Jakarta. DP2M Dikti.
Suprapti, Lies. 2005. Tepung Tapioka (Pembuatan dan Pemanfaatannya). Yogyakarta: Kanisius.
Zulisma A., dkk. 2013. Pengaruh Penambahan Gliserol terhadap Sifat Mekanik Film Plastik Bioadegradasi dari Pati Kulit Singkong. Jurnal Teknik kimia USU, Vol. 2, No. 2,hal. 39.
Article Metrics
Abstract view : 1560 times | PDF view : 1188 timesLicense URL: https://creativecommons.org/licenses/by-nc-nd/4.0/
Organized by :
Physics Department
Faculty of Mathematics and Natural Sciences,Universitas Negeri Makassar,
Daeng Tata Raya Street, Parangtambung, Tamalate, South Sulawesi, Indonesia.
Postal Code: 90224 Phone/Fax (0411)840622
Website: http://ojs.unm.ac.id, email: jspf@unm.ac.id
Jurnal Sains dan Pendidikan Fisika (JSPF) is licensed under a creative commons Attribution-NonCommercial-NoDerivatives 4.0 International License